Automotive glass enamel for laminating cycles - S2
High-performance ceramic enamels for automotive glass
Laminating products - S2
|
|
|
Chemical Resistance
|
|||||
| Product [1] | Firing |
Glass
Surface
|
Key Features
|
HCI [2]
|
Citric Acid[3]
|
Alkali[4]
|
H₂SO₄ [5]
|
| 1L6026 |
• Matt
• 550°C - 620°C |
S2
Pre-fire |
High optical density at lower layer thickness, achieving better coverage efficiency.
Excellent non-stick performance. |
5
|
2
|
2
|
4
|
| 1L6060 | • Matt • 550°C - 620°C |
S2 Pre-fire |
Stable jet-black colour over a wide working window to better guarantee process stability. | 5 | 3 | 2 | 4 |
| S2-IR | • Matt • 570°C - 640°C |
S2 No Pre-fire |
Requires no pre-firing, cost-saving product. Improved printing properties, achieves optical density at lower wet layer thicknesses. |
- | - | - | 4 |
[1] - Glass temperature - data based on laboratory kiln conditions and should be used for comparative purposes only.The decoration media used could impact on the performance and working window of the fired product.
[2] - 3.7% HCl, 5 minutes, 20°C, assessment according to ASTM C724-91
[3] - 10% Citric acid, 15 minutes, 20°C, assessment according to ASTM C724-91
[4] - 0.1N NaOH, 24 hours, room temperature, assessment according to ASTM C724-91
[3] - 10% Citric acid, 15 minutes, 20°C, assessment according to ASTM C724-91
[4] - 0.1N NaOH, 24 hours, room temperature, assessment according to ASTM C724-91
[5] - 0.1N H₂SO₄, 80°C, check after 4, 24, 48, 72, 96 and 144 hours. Failure mode: when visible change in colour through the glass can be detected.
PRODUCT CODE: 1L6026
1L6026 is an automotive laminating glass enamel suitable for side 2 decoration of
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
- Fired Surface Appearance: Matt, Black
- H₂SO₄ Acid Resistance [0.1N H₂SO₄, @ 80°C]: < 4 hours
Outstanding Features
- High optical density at lower layer thicknesses
- achieving better coverage effi ciency.
- Suitable for S2 application with pre-fi ring
- Excellent non-stick performance
Packaging Format
9 Litre Metal Drum approx. 12 - 14 Kgs
16 Litre Metal Drum approx. 25 Kgs
16 Litre Metal Drum approx. 25 Kgs
Packaging is based on powder dispersed in medium.
In-liner option available
In-liner option available
PRODUCT CODE: 1L6060
1L6060 is an automotive laminating glass enamel suitable for side 2 decoration of
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
- Fired Surface Appearance: Matt, Black
- H₂SO₄ Acid Resistance [0.1N H₂SO₄, @ 80°C]: < 4 hours
Outstanding Features
- Stable jet-black colour over a wide working window to better guarantee process stability
- Good non-stick performance
- Suitable for S2 application with pre-firing
Packaging Format
9 Litre Metal Drum approx. 12 - 14 Kgs
16 Litre Metal Drum approx. 25 Kgs
16 Litre Metal Drum approx. 25 Kgs
Packaging is based on powder dispersed in medium.
In-liner option available
In-liner option available
PRODUCT CODE: S2-IR
1L6060 is an automotive laminating glass enamel suitable for side 2 decoration of
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
windshields (with pre-fi ring) by screen printing, where silver hiding is not needed and is suitable for sag-bend and press-bending applications.
The product is an unleaded cadmium free bismuth-zinc based frit system pigmented with temperature stable inorganic pigments.
- Fired Surface Appearance: Matt, Black
- H₂SO₄ Acid Resistance [0.1N H₂SO₄, @ 80°C]: < 4 hours
Outstanding Features
- Stable jet-black colour over a wide working window to better guarantee process stability
- Good non-stick performance
- Suitable for S2 application with pre-firing
Packaging Format
9 Litre Metal Drum approx. 12 - 14 Kgs
16 Litre Metal Drum approx. 25 Kgs
16 Litre Metal Drum approx. 25 Kgs
Packaging is based on powder dispersed in medium.
In-liner option available
In-liner option available
Application sectors
Products menu
Request info
Request information
FENZI S.p.A Via Trieste Zona Industriale, 20067 Tribiano (MI) Italy
Tel +39 02 906221
Copyright © 2025, FENZI S.p.A. Tutti i diritti riservati - P.Iva 11328880155
Tel +39 02 906221
Copyright © 2025, FENZI S.p.A. Tutti i diritti riservati - P.Iva 11328880155